JB/T 6399-1992 Spring steel for heavy machinery

This standard specifies the technical requirements for ordering, manufacturing and acceptance of spring steel. This standard applies to purchased and self-made springs, elastic parts and spring steel with larger cross-sections. JB/T 6399-1992 Spring steel for heavy machinery JB/T6399-1992 Standard download decompression password: www.bzxz.net

Mechanical Industry Standard of the People's Republic of China
JB/T 6399-1992
Spring Steel for Heavy Machinery
Published on July 14, 1992
Implementation by the Ministry of Machinery and Electronics Industry of the People's Republic of China on July 1, 1993
Mechanical Industry Standard of the People's Republic of China
Spring Steel for Heavy Machinery
1 Subject Content and Scope of Application
This standard specifies the technical requirements for ordering, manufacturing and acceptance of spring steel. This standard applies to purchased and self-made springs, elastic parts and spring steel with larger cross-sections. 2 Reference standards
GB 222
Ordering requirements
Sampling of samples for chemical analysis of steel and chemical tolerances of finished products Chemical analysis methods for steel and alloys
Metal tensile test methods
Metal Brinell hardness test methods
JB/T 6399-1992
The purchaser shall provide the supplier with product drawings and indicate the delivery status, i.e., heat treatment or no heat treatment. If there are other technical requirements, they can be agreed upon by both parties.
4 Manufacturing
Self-smelted or outsourced spring steel shall be smelted in electric furnaces or induction furnaces. 5 Technical requirements
5.1 Chemical composition
5.1.1 The steel grade and chemical composition (melting analysis) shall comply with the provisions of Table 1. 5.1.2 The allowable deviation of the chemical composition of steel shall comply with the provisions of GB222. 5.2 Mechanical properties
5.2.1 If the spring steel is heat treated, its mechanical properties shall comply with the provisions of Table 2, and the specimens shall be taken from the rough pieces heat treated in the same furnace. 5.2.2 The tensile properties in Table 2 are only applicable to steel types with spring cross-sectional dimensions not exceeding 80 mm. When the cross-sectional dimensions are greater than 80 mm, the elongation and cross-sectional shrinkage are allowed to be reduced by 1 unit and 5 units respectively. When the purchaser requires hardness, it shall comply with the provisions of Table 3, but tensile properties cannot be required at the same time. 5.2.3
When the purchaser requires other tempering temperature heat treatment, it shall be agreed upon by the supply and demand parties. 5.2.4
Approved by the Ministry of Machinery and Electronics Industry on July 14, 1992 and implemented on July 1, 1993
60Si2Mn
60Si2MnA
60Si2CrA
60Si2CrVA
50CrVA
60Si2Mn
60Si2MnA
60Si2CrA
0.62~0.70
0.62 ~0.70
0.62~0.70
0.56-0.64
0.56~0.64
0.56~0.64
0.56~0.64
0.46~0.54
0.17-0.37
0.17~0 .37
0.17~0.37
1.60~2.00
1.40~1.80
1.40~1.80
0.17~0.37
JB/T6399-1992
Chemical composition of spring steel
0.50~0.80
0.90~1.20
0.60~0.90
0.40~0.70
0.50~0.80
Mechanical properties of spring steel
Heat treatment specification
Floating fire temperature
840 (Oil cooling)
830 (Oil cooling)
830 (Oil cooling)
870 (Oil cooling)
870 (Oil cooling)
870 (Oil cooling)
60Si2CrVA
50CrVA
850 (Oil cooling)
850 (Oil cooling)
Tempering temperature
Note: The allowable deviation of heat treatment temperature is quenching temperature ±20℃,
Tempering temperature ±50℃.
60Si2Mn;60Si2MnA
50CrVA
60Si2CrA
60Si2CrVA
(longitudinal)
Hardness of spring steel
Delivery state
No heat treatment
Heat treatment
0.70~1.00
0.80~1.10
Mechanical properties
0.10-0.20bzxZ.net
0.10~0.20
5.3 Appearance and defect removal
JB/T 6399-1992
5.3.1 The surface of spring steel shall not have cracks, folds, scars, inclusions, delamination and pressed iron oxide scale. 5.3.2 Local defects on the surface of spring steel must be removed. The removal depth shall not affect the minimum allowable size of the spring section. The width of the removal shall not be greater than 5 times the removal depth.
5.4 When the purchaser has special requirements, such as non-metallic inclusions, microstructure, grain size, decarburization layer depth, low magnification, etc., it shall be agreed upon by both parties. 6 Test methods and acceptance
6.1 Test methods
Chemical composition shall be implemented in accordance with GB223; hardness shall be implemented in accordance with GB231: mechanical properties shall be implemented in accordance with GB228. 6.2 Acceptance
The inspection and acceptance of spring steel shall be carried out by the supplier in accordance with this standard and the requirements of the order contract. Additional notes:
This standard is proposed and managed by the Deyang Large Casting and Forging Research Institute of the Ministry of Machinery and Electronics Industry. This standard was drafted by the Deyang Large Castings and Forgings Research Institute of the Ministry of Machinery and Electronics Industry. The main drafter of this standard is Zhu Jiexiu.
People's Republic of China:
Mechanical Industry Standard
Spring for Mechanical Use
JB/T 63991992
Published and issued by the China Academy of Mechanical Science
Printed by the China Academy of Mechanical Science
(No. 2, Shouti South Road, Beijing
Postal Code 100044)
Format 880×1230
Print Sheet 3/8
Word Count 6.000
First Edition in September 1992
First Printing in September 1992
Print Quantity 1-500
Price 0.90 Yuan
Mechanical Industry Standard Service Network: http://www.JB.ac.cn261_6659 /
Tip: This standard content only shows part of the intercepted content of the complete standard. If you need the complete standard, please go to the top to download the complete standard document for free.