GB/T 15010-1994 Corrosion resistant alloy cold rolled sheet

GB/T 15010-1994 Corrosion-resistant alloy cold-rolled sheet GB/T15010-1994 standard download decompression password: www.bzxz.net

National Standard of the People's Republic of China
Cold-rolled sheets of cerrusion-resisting alloy
Cold-rolled sheets of cerrusion-resisting GB/T 15010-94
Replacement CBn275
This standard applies to cold-rolled sheets of ferrous and nickel-based corrosion-resistant alloys with a thickness of 0.8~4 mm (hereinafter referred to as sheets). 1 Dimensions and shape
1.1 The dimensions and allowable deviations of the sheets shall comply with the provisions of GB 708:-88 "Dimensions, shape, weight and allowable deviations of cold-rolled steel sheets and strips".
1.2 The insert bend of the sheet per meter length shall not exceed 4 mm1.3 The width of the sheet per meter length shall not exceed 10 mm, but the width of the sheet per meter length with a tensile strength greater than 685 N/mm may be greater than 15 mm.
2 Technical requirements
2.1 Grade and chemical composition
2.1.1 The grade and chemical composition (melting analysis) of the alloy shall comply with the provisions of Table 1. 2.1.2 When conducting finished product analysis, deviations from the provisions of Table 1 are allowed, but the maximum allowable deviation value shall comply with the provisions of Table 2 in GB/T15007 Corrosion-resistant alloy grades.
2.2 Delivery status
The plate shall be delivered after solution treatment, pickling, leveling and trimming. 2.3 Mechanical properties
The mechanical properties of the plate after solution treatment shall comply with the yield strength values ​​specified in Table 2 and shall be measured only when required by the purchaser (specified in the contract).
2.4 Macro inspection
The transverse acid-etched macrostructure of the plate shall not have residual shrinkage cavities, cracks, delamination and inclusions visible to the naked eye. 2.5 Grain size
The plate in the delivery state shall be inspected for grain size and the measured results shall be reported. 2.6 Surface quality
2.6.1 The plate shall not be delaminated. The surface shall be smooth and flat. There shall be no cracks, bubbles, inclusions, scars, oxide scale and over-pickling marks. 2.6.2 The surface is allowed to have local slight pits, scratches, pits and marks with a depth not greater than half of the plate thickness tolerance and not less than the minimum thickness allowed. Any defects exceeding the above provisions may be removed by grinding, and the depth of local defect elimination shall not make the plate less than the minimum thickness allowed.
2.7 Special requirements
Under the condition of technical basis, according to the requirements of the purchaser, special requirements such as chemical composition and mechanical properties may be supplemented, or special inspection items such as corrosion test and non-destructive testing may be supplemented, but the specific requirements and test methods shall be determined by negotiation between the supply and demand parties. 3 Test methods
The test methods, sample rules and quantity of plates shall comply with the requirements of Table 3. Approved by the State Bureau of Technical Supervision on April 4, 1994, and implemented on May 1, 1994
.0. 10
GB/T15010-94
19. 0~ 23. 0|30. 0 ~35. 0
:0. 05~0. 10
19. 0 ~23. 0. 30. 0-- 35, 0
.0.030
0. 15 ~0. 60
0. 15~0. 60
0. 40 ~ 0. 90
0. 60 ~1. 20
0.40~0,90
19. 0r~21. 0, 42. 0-~44. 0
25.0--27.0
34. 0--37.0
19. 5~-23. 5
#! 38.0~-46. 0
28. 0~31. 0
14. 0~17. 0
21.0~25. 0
35. 0~38. 0
14. 017. 0
14. 5 ~16. 5
14.5~16.5
14. t~18. t
6. 0 ~ 10. 0
10. 0 ~ 15. 0
4. 0~ 6. 0
4. 0~7. 0
4. 0 ~7. 0
0. 20 ~ 0. 40
:12.5~13. 5
2. 0 ~ 3. 0
2. 5 ~-3, 5
26. 0~30. 0
26, 0-~30. 0
2. 0 ~ 3. 0bzxZ.net
15. 0 ~17. 0
15.0~17,0
[14. 0 ~ 17. 0
8. 0~~ 10. 0
.1. 00
3. 0~ 4. 5
3. 0~ 4. 0
1. 5~3. 0
:0.15--0.60
0. 15 ~~ 0. 60
1. 00~1. 70
0. 20 ~ 0. 50
.0.030
.0. 020
Recommended solution location
Treatment intensity,
1 000~[ 060
11001170
1160~1 210
1000--1050
1020~1070
1050~1100
1 000~1050
1100~-1160
1 080~1130
1140~1190
10401 090
1050~1100
1160~1210
1150~1200
1050～1100
1100~1150
Inspection Items
Chemical Analysis
Low Power Inspection
Mechanical Properties
Surface Quality
Ultrasonic Wave Detection
Stain Erosion Test
Grain Size
GB/T 15010—94
Test method
GE 1467— 78
GL/114999.2
GB 228—87
Visual inspection
Visual inspection
General measuring tools
GB2108—80
Or agreement
GB6394
Mechanical properties
.,N/mm
Not less than a thousand
Partner rules
GB22284
Machine is at the head of the copper ingot
GB2975—82
G156397—86
Most companion number
Each piece
Each piece
Two pieces per batch
Two pieces per batch
4 Inspection rules
GB/T 15010—94
The general provisions for material acceptance shall comply with the provisions of GB247-80 General Provisions for Acceptance, Packaging, Marking and Quality Certificate of Steel Plates and Steel Strips 4.1
4.2 The test results of chemical composition, mechanical properties, surface quality, size and appearance shall comply with the relevant provisions of this standard. However, mechanical properties may be omitted with the consent of the purchaser. 5 Packaging, marking and quality certificate
The packaging, marking and quality certificate of plates shall comply with the relevant provisions of GB247-80, with additional instructions;
This standard was proposed by the Information and Standards Research Institute of the Ministry of Metallurgical Industry. This standard was drafted by the Changcheng Plant of the Metallurgical Industry. The level mark of this standard is GB/T15010—941