GB/T 3848-1983 Determination method of coercive (magnetic) force of cemented carbide
time:
2024-08-10 18:23:36
- GB/T 3848-1983
- in force
Standard ID:
GB/T 3848-1983
Standard Name:
Determination method of coercive (magnetic) force of cemented carbide
Chinese Name:
硬质合金矫顽(磁)力测定方法
Standard category:
National Standard (GB)
-
Date of Release:
1983-09-14 -
Date of Implementation:
1984-09-01
Standard ICS number:
Electrical Engineering >> 29.040 Insulating Fluids 29 Electrical EngineeringChina Standard Classification Number:
Metallurgy>>Methods for testing physical and chemical properties of metals>>H21 Methods for testing physical properties of metals
Release date:
1983-09-14Review date:
2004-10-14Drafting Organization:
Zigong Cemented Carbide FactoryFocal point Organization:
National Technical Committee for Standardization of Nonferrous MetalsPublishing Department:
National Bureau of StandardsCompetent Authority:
China Nonferrous Metals Industry Association

Skip to download
Summary:
This standard is applicable to the determination of the coercive (magnetic) force of cemented carbide containing more than 3% ferromagnetic material as a binder. GB/T 3848-1983 Determination of the coercive (magnetic) force of cemented carbide GB/T3848-1983 Standard download decompression password: www.bzxz.net

Some standard content:
National Standard of the People's Republic of China
Method for determination of coercivity (magnetization) of cemented carbideHardmetals-determination of (the magnetization) coercivityUDC621.762.1
:620.179.14
GB 3848-83
ISO3326-1975
This standard is applicable to the determination of coercivity (magnetization) of cemented carbide containing more than 3% ferromagnetic material as a binder. This standard is equivalent to ISO3326-1975 "Determination of coercivity (magnetization) of cemented carbide". Principle
The sample is magnetized to the technical magnetic saturation state in the current magnetic field, and then the size of the reverse magnetic field required to completely demagnetize the sample (M=0) is the coercivity (magnetization) HcM to be measured. 2 Symbols and names
The unit of coercive (magnetic) force HkM is A/m, which is the magnitude of the reverse magnetic field required to reduce the magnetization intensity of the sample to zero (see the figure below).
Magnetic field intensity
Magnetic intensity of the sample
Saturation magnetization intensity
Coercive (magnetic) force
The equipment should be able to magnetize the sample to the technical saturation state in the DC magnetic field and demagnetize it. 3.1
3.2The accuracy of the equipment is 0.2kA/m for the correction magnetic force within 20kA/m; 1% for more than 20kA/m. 3.3In order to make the sample reach technical magnetic saturation, the magnetic field intensity should be 200~400kA/m, which is generally determined according to the type of equipment used. Issued by the National Bureau of Standards on September 14, 1983Www.bzxZ.net
Implementation on September 1, 1984
Sampling shall be carried out in accordance with relevant regulations.
5 Steps
GB 3848--83
Place the sample in a DC magnetic field so that its long axis is aligned with the direction of the magnetic field, and magnetize the sample to the technical magnetic state. 5.1
5.2 Demagnetize the sample in an opposing DC magnetic field. The speed of demagnetization must be slow enough to obtain the accuracy listed in 3.2. 5.3 Determine the coercive (magnetic) force tM of the demagnetized sample. 6 Expression of results
The result of the determination of the coercive (magnetic) force lkw should be rounded to 0.1 kA/m. 7
Test report
This standard number,
Details required to identify the sample;
Measured results;
All operating conditions not specified in this standard or optional; Any conditions that have affected the results. Additional remarks:
This standard was proposed by the Ministry of Metallurgical Industry of the People's Republic of China. This standard was drafted by the responsible person of the cemented carbide factory.
Tip: This standard content only shows part of the intercepted content of the complete standard. If you need the complete standard, please go to the top to download the complete standard document for free.
Method for determination of coercivity (magnetization) of cemented carbideHardmetals-determination of (the magnetization) coercivityUDC621.762.1
:620.179.14
GB 3848-83
ISO3326-1975
This standard is applicable to the determination of coercivity (magnetization) of cemented carbide containing more than 3% ferromagnetic material as a binder. This standard is equivalent to ISO3326-1975 "Determination of coercivity (magnetization) of cemented carbide". Principle
The sample is magnetized to the technical magnetic saturation state in the current magnetic field, and then the size of the reverse magnetic field required to completely demagnetize the sample (M=0) is the coercivity (magnetization) HcM to be measured. 2 Symbols and names
The unit of coercive (magnetic) force HkM is A/m, which is the magnitude of the reverse magnetic field required to reduce the magnetization intensity of the sample to zero (see the figure below).
Magnetic field intensity
Magnetic intensity of the sample
Saturation magnetization intensity
Coercive (magnetic) force
The equipment should be able to magnetize the sample to the technical saturation state in the DC magnetic field and demagnetize it. 3.1
3.2The accuracy of the equipment is 0.2kA/m for the correction magnetic force within 20kA/m; 1% for more than 20kA/m. 3.3In order to make the sample reach technical magnetic saturation, the magnetic field intensity should be 200~400kA/m, which is generally determined according to the type of equipment used. Issued by the National Bureau of Standards on September 14, 1983Www.bzxZ.net
Implementation on September 1, 1984
Sampling shall be carried out in accordance with relevant regulations.
5 Steps
GB 3848--83
Place the sample in a DC magnetic field so that its long axis is aligned with the direction of the magnetic field, and magnetize the sample to the technical magnetic state. 5.1
5.2 Demagnetize the sample in an opposing DC magnetic field. The speed of demagnetization must be slow enough to obtain the accuracy listed in 3.2. 5.3 Determine the coercive (magnetic) force tM of the demagnetized sample. 6 Expression of results
The result of the determination of the coercive (magnetic) force lkw should be rounded to 0.1 kA/m. 7
Test report
This standard number,
Details required to identify the sample;
Measured results;
All operating conditions not specified in this standard or optional; Any conditions that have affected the results. Additional remarks:
This standard was proposed by the Ministry of Metallurgical Industry of the People's Republic of China. This standard was drafted by the responsible person of the cemented carbide factory.
Tip: This standard content only shows part of the intercepted content of the complete standard. If you need the complete standard, please go to the top to download the complete standard document for free.
- Recommended standards
- GB/T 2679.1-1993 Determination of paper transparency
- CJJ/T 59-1994 Standard for determination of design parameters of flexible pavement CJJ/T59-94
- QB/T 1622.9-1992 Stainless steel utensil tray
- JB/T 9755-1999 Technical requirements for paper filter element air filter assemblies for internal combustion engines
- GBJ 140-1990 Design specification for fire extinguisher configuration in buildings GBJ140-90
- GB 50277-1998 Specification for construction and acceptance of foundry equipment installation projects
- NY/T 5002-2001 Technical specification for the production of pollution-free food chives
- GB 17379-1998 General rules for storage of bulk petroleum and liquid chemical products in ports
- SY/T 6538-2002 Formulated selective desulfurization solvent
- JB/T 5335-1991 Basic technical requirements for DC motors for battery vehicles
- HG 2858-2000 40% Carbendazim SC
- GB/T 8424.2-2001 Textiles - Colour fastness tests - Instrumental evaluation method for relative whiteness
- GB/T 8145-2003 Gum rosin
- JB/T 9542-1999 Technical requirements for dual-value capacitor asynchronous motors
- GB/T 15772-1995 General principles for comprehensive soil and water conservation planning
Please remember: "bzxz.net" is the combination of the first letters of the Chinese pinyin of the four Chinese characters "standard download" and the international top-level domain name ".net". ©2024 Standard download websitewww.bzxz.net Mail:bzxznet@163.com