JB/T 5657-1991 Electrical pressure-sensitive adhesive tape Polyester film thermoplastic adhesive tape

This standard specifies the technical requirements, test methods, inspection rules and marking, packaging, transportation and storage of polyester film pressure-sensitive adhesive tapes for electrical use with thermoplastic adhesives. This standard applies to adhesive tapes made of polyester film with thermoplastic adhesives coated on one side. JB/T 5657-1991 Electrical pressure-sensitive adhesive tapes Polyester film thermoplastic adhesive tapes JB/T5657-1991 Standard download decompression password: www.bzxz.net

Mechanical Industry Standard of the People's Republic of China
JB/T5657-1991
Electrical Pressure-Sensitive Adhesive Tape
Polyester Film Thermoplastic Adhesive Tape
Issued on June 16, 1992
Implementation by the Ministry of Machinery and Electronics Industry of the People's Republic of China on December 1, 1992
Mechanical Industry Standard of the People's Republic of China
Electrical Pressure-Sensitive Adhesive Tape
Polyester Film Thermoplastic Adhesive Tape
JB/T 5657-1991
This standard refers to the International Electrotechnical Commission (IEC) publication 454-3-3 (first edition, 1981) Specification for Electrical Pressure-Sensitive Adhesive Tape Part 3: Part 3 of Single Material Specification: "Requirements for Polyester Film (PETP) Adhesive Tapes Coated with Non-Thermosetting Adhesives". 1
Subject content and scope of application
This standard specifies the technical requirements, test methods, inspection rules and marking, packaging, transportation and storage of polyester film pressure-sensitive adhesives coated with thermoplastic adhesives for electrical use (hereinafter referred to as adhesive tapes). This standard applies to adhesive tapes made of polyester film coated with thermoplastic adhesives on one side. Note: The thermoplastic adhesives used for this type of adhesive tapes are usually based on natural or synthetic rubber. Reference standards
JB/T5969 Pressure-sensitive adhesive tapes for electrical use
JB/T5970 Pressure-sensitive adhesive tapes for electrical use
Product model and code
The model of this product is: 6231
General requirements
Test methods
The code of this product is: F-PETP/130/Tp4
Technical requirementsbzxZ.net
The appearance should comply with the provisions of Chapter 4 of JB/T5969. 4.2 Dimensions
4.2.1 Width and Deviation
The width and deviation shall comply with the provisions of Article 5.2 of JB/T5969. 4.2.2 Length
The length shall comply with the provisions of Article 5.3 of JB/T5969. 4.2.3 Thickness and Deviation
The preferred nominal thickness is 0.02~0.1mm, and the thickness deviation is ±15% or ±0.01mm. The larger absolute value of the two shall be selected as the allowable deviation.
Performance of Adhesive Tape
The performance of Adhesive Tape shall comply with the provisions of Table 1.
Indicator name
Electrolytic corrosion"
Resistance method
Long-term heat resistance (temperature index)
Approved by the Ministry of Machinery and Electronics Industry on June 16, 1992-
Implemented on December 1, 1992
Indicator name
Tensile strength
Elongation at break
Adhesion to plate
Thickness ≤ 0.02mm
Thickness > 0.02mm
Strength to substrate
Electrical strength
Changsen time
After being affected by moisture
JB/T5657-1991
Continued Table 1
N/10mm
N /10mm
N/10mm
Note: 1) For materials that meet the requirements of this item, the tensile strength method or visual inspection method can be added as needed. Test method
When there is no special provision, the test details should be pre-treated and tested in accordance with the requirements of Chapter 3 of JB/T5970. Appearance
The appearance is observed with the eyes and mouth.
5.2.1 Width
The width is measured with a steel ruler with a graduation value of 0.5mm. 5.2.2 Length
The length is measured with a meter or a saw ruler accurate to 1cm. 5.2.3 Thickness
The thickness is measured according to the method in Chapter 4 of JB/T5970. Electrolytic corrosion
Thickness>600 per meter||tt ||The sample was treated at 23±2℃ and relative humidity of 91%～95% for 24h and then tested according to the method in Chapter 5 of JB/T5970. 5.4
Long-term heat resistance
The temperature index of the material was determined according to the method in Chapter 8 of JB/T5970. The recommended aging temperatures are: 150℃, 160℃ and 180℃. Failure standard 1-electrical strength: 35MV/m, tensile strength and elongation at break were calculated for the original thickness
Tested according to the method in Chapter 10 of JB/T5970,
Adhesion to steel plate and adhesion to substrate were tested according to the method in Chapter 11 of JB/T5970.
Electrical strength
Tested according to the method in Chapter 13 of JB/T5970,||t t||Inspection rules
The recommended factory inspection items are Items 5, 6, and 7 in Table 1 of Articles 4.1, 4.2, and 4.3 of this standard. The determined product temperature index is always valid when the composition or parts and manufacturing process are not changed. Others should be carried out in accordance with the provisions of Chapter 6 of JB/T5969. 2
Marking, packaging, transportation and storage
JB/T5657-1991
Should comply with the provisions of JB/T5969 on marking, packaging, transportation and storage. The storage temperature and relative humidity limit values ​​refer to the maximum values ​​caused by climate change, rather than the highest conditions allowed for continuous storage. Additional notes:
This standard is proposed by the National Technical Committee for Standardization of Insulating Materials. This standard is under the jurisdiction of the Guilin Electric Science Research Institute of the Ministry of Machinery and Electronics Industry. This standard was drafted by the Guilin Electric Science Research Institute, Changzhou Second Insulating Materials Factory and other units. The main drafters of this standard are Huang Zuo and Wang Linlin. People's Republic of China
Mechanical Industry Standard
Electrical Pressure-Sensitive Adhesive Tape
Polyester Film Thermoplastic Adhesive Tape
JB/T 56571991
Published and issued by the Mechanical Science Research Institute
Printed by the Mechanical Science Research Institute
(No. 2 Shouti South Road, Beijing
Langbian 100044)
Format 880×12301/16 Printing Sheet X/X Number of Words XXX,XXX19XX Edition Xth Edition Xth Printing in XXth Month of 19XX Number of Prints 1-XXX
Price XXX.XX Yuan
No. XX-XXX
Mechanical Industry Standard Service Network: http://www.JB.ac.cn1661_9
Tip: This standard content only shows part of the intercepted content of the complete standard. If you need the complete standard, please go to the top to download the complete standard document for free.