QB/T 3635-1999 Rigid polyvinyl chloride (PVC-U) skirting board

This standard specifies the classification, technical requirements, test methods and inspection rules of rigid polyvinyl chloride (PVC-U) skirting boards. This standard applies to polyvinyl chloride skirting boards (hereinafter referred to as skirting boards) made of polyvinyl chloride resin as the main raw material. QB/T 3635-1999 Rigid polyvinyl chloride (PVC-U) skirting boards QB/T3635-1999 Standard download decompression password: www.bzxz.net

Classification number: Q74
Light Industry Standard of the People's Republic of China
QB/T 3635-1999
Replacement 2BY28006-1988
Rigid polyvinyl chloride (PVC-U) skirting board
Published on April 21, 1999
State Bureau of Light Industry
Implemented on April 21, 1999
QB/T3635-1999
This standard extends the original professional standard ZBY28006-19886 polyvinyl chloride (2VC-U) skirting board, and is converted into standard number ×QB/3635-1999 through the publication of the State Light Industry Bureau No. 1993112, and the content remains unchanged. This standard is based on the Su Standard Factory 0 1911-77 "Technical Specifications for Polyvinyl Chloride Strip System 3". This standard was proposed by the Industry Management Department of the State Bureau of Light Industry: This standard was drafted by the National Plastic Products Chemical Technical Committee. This standard was drafted by Tianjin Material Research Institute. The main drafter of this standard is Wang Honghuang. From the date of implementation of this standard, it will replace the original light industry standard ZBY28006-98 Hard Polyethylene (PVC-U) Skirting Board, and the light industry standard of the People's Republic of China Hard Polyethylene (PVC-UJ) Skirting Board QB/T 3635-1999, which replaces QB/T 7.RY2200-18. This standard specifies the classification, technical requirements, test methods and inspection rules for hard polyvinyl chloride (PYL-U) skirting boards. This standard applies to ethylene-based panels (hereinafter referred to as ethylene-based panels) made of ethylene resin as the main raw material and molded by anti-aging.
2 Reference standards
3133 Thermoplastic Decomposition Temperature (Vicat) Test Method C82416 Plastic Flammability Test Method GE3393 Plastic Combustion Degradation Quality Test Method
3 Product Classification
3. Non-standard panels 3.2 The cross section deviation of the panel is ±0.2mm, and the other dimensions are 12.0mm. 4 Technical Requirements
4.1 Color
The panel is black, and the color can be determined by the customer. 4.2 Appearance
4.2.1 The front of the panel should be smooth and without knots. When it is dropped, it is easy to scratch. , turning points and embedded foreign objects, 42, 2 The edge of the skirting board shall not have expansion, opening, some, effect, and the two end surfaces shall be straight and flat with the axis connection. 4.2, 3 The inner length of the skirting board shall be straight. 4, 3 The performance of the rotating machine shall meet the requirements of the specification 1. Table
Dimensional comparison point www.bzxz.net
Longitudinal yield rate after heating
Prohibition index (
Pressure test method
Test result
National Light Industry Road 199-04-21 approved
1999-04-21 implemented
Test method
5.1 Test method
QB/T3635—1999
The samples used should be prepared from the test tube. 5.2 Condition of the sample If there is no special provision for the standard environment of the test, the test sample should be placed at 23°C for more than 4 hours, and then the test should be carried out in this environment. 5.3 Determination of size difference between standard and standard sizes.
Use a special caliper with a diameter of 0.2mm to measure. 5.4 Determination of length and width
Use a steel tape measure with a diameter of 1m or a tool with equal accuracy to measure. 5.5 Determination of appearance
Under self-heating light, the sample is subjected to a drop at a distance of 400-509mm from the foot plate. 5.6 Determination of Vicat melting point
Perform according to CB1633. The heater is heated at a speed of A, and the sample is subjected to a static load center A. 5.7 Determination of longitudinal shrinkage
5.7.1 Trial
Use the method of cutting to cut a 20+0 device board. 5.7.2 Squeeze||t t||This number is the actual R5.7.3 Test procedure
Draw two lines along the length direction of the sample at 23+1mm, measure the maximum distance, guess D, mm, and place it flat on the powder plate. Then take the test plates out of the oven, cool to , measure the standard distance, and confirm. 5.7.4 Calculation and expression of the test potential
The longitudinal shrinkage is calculated by the following formula:
Longitudinal shrinkage standard, %:
The distance between the longitudinal line and the plate after the object moves,
The result is expressed as the arithmetic mean of the main samples. 5.8 Determination of the effectiveness of the test
Continue to 240:
5.9 Determination of the ball pressure
According to GR398.
5.10 Drop impact test (extended)
5.10.1 Sample
Mechanical method: Sample thickness equal to 2 times of sample thickness, but not less than 1mm, test number 10.
-TTTKNrKca-
.10.2 Apparatus
QB/T3635—1999
Drop impact test machine; ball, mass 1 kg5.10.3 Test conditions
After the sample is placed at -101A for 4a, it is immediately tested at a temperature of 2±2°C within 10s.
5.10,4 Test procedure
Put the test piece on the test bench, and place it on the center of the test piece with a mass of 1k, 3m away from the guide rail
5.1.5 Evaluation of the test potential
The test piece will be considered unqualified if it has cracks after impact: 6 Inspection rules
6.1 The production unit is responsible for the inspection of the product. 6.2 The same specification plates produced under the same formula and process conditions are regarded as a batch. This number shall not exceed the production quantity is small, and the monthly output is a batch. 6.3 Under the condition that the formula, raw materials, process and specifications remain unchanged, the physical property indicators shall be tested once every fold. If any of the items are changed, the physical property indicators shall be updated one by one according to Table 1. If one item fails to meet the standards, the product shall be deemed as unqualified.
6.5 The appearance and size shall be inspected thoroughly. If any of the items fails to meet the standards, the product shall be deemed as unqualified. .6 When the supplier has a dispute over the product or service, the qualified unit shall be requested to conduct a double test of the sample according to Table 1. If any of the indicators fails to meet the standards, the product shall be deemed as unqualified.
The packaging should be made into a single package, and the packaging should be made of paper, plastic film, etc. without exposing it. Each package has a certificate of conformity and is marked with: a. Manufacturer name:
L. Product name;
:. Trademark;
d. Production date, shift, quantity
c. Inspector code:
. Quality and other marks and qualified inspections.
7.2 During packaging, storage and transportation, the product should not be thrown, thrown, exposed, dried, swelled or worn. 7.3 The weak foot should be stored horizontally within 4D of the temperature. The stacking distance should not exceed 1m, and the distance from the heat source should not be less than 1m. Those stored below 0°C must be kept at room temperature for 24h before use: 7.4 The shelf life is about one year from the factory.
Tip: This standard content only shows part of the intercepted content of the complete standard. If you need the complete standard, please go to the top to download the complete standard document for free.