GB/T 3283-1987 Vanadium pentoxide

GB/T 3283-1987 Vanadium Pentoxide GB/T3283-1987 Standard download decompression password: www.bzxz.net

National Standard of the People's Republic of China
Vanadium pentoxide
UDC 661. 888. 22
GB3283-87
Replaces GB328382
This standard applies to vanadium pentoxide in flake or powder form for metallurgy, chemical industry, etc., obtained by roasting, leaching, precipitation, decomposition and melting of vanadium slag or other vanadium-containing minerals.
1 Technical requirements
1.1 Brands and chemical composition
1.1.1 The products are divided into three brands according to their use and vanadium pentoxide grade, and their chemical composition shall comply with the provisions of the following table: Chemical
Scope of application Brand
Not less than
Note: The amount of vanadium pentoxide is converted from the total vanadium content. P
Not more than
1.1.2 If the buyer has special requirements, we can negotiate to supply products with lower impurity content. As
1.1.3 When the buyer requires, we can negotiate to provide measured data of other elements not listed in the table. 1.2 Physical state
Na20+K,0
Physical state
Vanadium pentoxide for metallurgy is delivered in flakes with a diameter of no more than 55×55mm and a thickness of no more than 5mm; vanadium pentoxide for chemical industry is delivered in natural powder after decomposition.
2 Test method
2.1 Sampling
The sampling of samples for chemical analysis shall be carried out in accordance with the method specified in Appendix A. 2.2 Sample preparation
The preparation of samples for chemical analysis shall be carried out in accordance with the method specified in Appendix B. 2.3 Chemical analysis
The analysis of vanadium pentoxide shall be carried out in accordance with the current analysis method of each manufacturer. If there is any objection, it shall be resolved through negotiation. 3 Inspection rules
3.1 The inspection and acceptance of product quality shall be carried out by the technical supervision department of the supplier, and the buyer has the right to re-inspect the product quality according to the regulations. If there is any objection, it should be raised within 30 days after arrival.
3.2 Products of the same brand can be delivered in one batch, and the batch is generally between 4 and 10 tons, or agreed by the supplier and the buyer. Approved by the Ministry of Metallurgical Industry of the People's Republic of China on July 23, 1987 and implemented on July 1, 1988
4 Packaging, marking, storage and transportation and quality certificate 4.1 Packaging
GB3283-87
The product is packed in iron drums, and a layer of protective paint must be applied to the inner wall of the drum. The net weight of each barrel is generally not more than 250kg, or can be negotiated by both parties. 2. Marking, storage and transportation and quality certificate
Product marking, storage and transportation and quality certificate shall comply with the requirements of GB3650--83 "General Provisions for Acceptance, Packaging, Storage and Transportation, Marking and Quality Certification of Ferroalloys".
A.1 Sampling of flaky vanadium pentoxide
GB3283-87
Appendix A
Sampling method of vanadium pentoxide
(Supplement)
From 25% of the packages of each batch of products, shovel a number of roughly equal samples at a depth of 100-200mm below the material surface. The total weight shall not be less than 2kg, and then crush to less than 10mm, mix thoroughly and then reduce to 1kg by quartering method. A.2 Sampling of powdered vanadium pentoxide
In 25% of the packages of each batch of products, insert a tray in the center of the barrel to more than half of the thickness of the material layer, and take approximately equal samples, the total amount of which shall not be less than 1kg.
Appendix B
Method for preparing samples of vanadium pentoxide
(Supplement)
B.1 Preparation of samples of flake vanadium pentoxide
Crush all 1kg of sample to less than 5mm, place it in a stainless steel plate, and use the quartering method to reduce 500g, put it in a pounding cylinder and pound it to 1.5mm, then use the quartering method to reduce 250g, put it in a pounding cylinder and pound it to less than 1mm, and use the quartering method to reduce 60g, and then crush it until it passes through an 80-mouth sieve. Pack it into two bags, one for analysis, and the other for future reference. B.2 Preparation of powdered vanadium pentoxide samplesbZxz.net
After mixing 1 kg of sample thoroughly, use the quartering method to reduce 60 g, and then crush or grind it until it passes through an 80-mesh sieve, and pack it into two bags, one for analysis and the other for future reference.
Additional remarks:
This standard was proposed by the Ministry of Metallurgical Industry of the People's Republic of China. This standard was drafted by Jinzhou Ferroalloy Factory. The main drafters of this standard were Huang Shujie and Bo Liqun. 118
Tip: This standard content only shows part of the intercepted content of the complete standard. If you need the complete standard, please go to the top to download the complete standard document for free.