GB/T 14903-1994 Test method for torsional shear strength of inorganic adhesive sleeves

This standard specifies the test method for the torsional shear strength of inorganic adhesive socket joints, the structure and size of the test piece, the preparation method of the sample, the test environment conditions, the test steps and the calculation method of the test results. This standard is applicable to the determination of the torsional shear strength of socket joints made of 45# steel bonded with inorganic adhesives. GB/T 14903-1994 Test method for torsional shear strength of inorganic adhesive socket joints GB/T14903-1994 Standard download decompression password: www.bzxz.net

UDC 620-176 :621-791.052 : 678.61C 38
National Standard of the People's Republic of China
GB/T 14903 94
Testing method for lorsional shear strengthof doedr joint by inorganic adhesives1994-01-02Published
National Technical Supervision Bureau
1994-10-01Implementation
National Standard of the People's Republic of China
Testing method for lorsional shear strengthof doedr joint by inorganic adhesives1Main content and scope of application
GB/T 14903—94
This standard specifies the test method for the torsion strength of inorganic adhesive joints, the test piece dimensions, the test piece preparation method, the test point conditions, the test steps and the calculation method of the test results. This standard is applicable to the determination of the torsion shear strength of socket joints made of 5-wire bonded by inorganic adhesives. 2 Principle
The socket joint specimen is made of a shaped specimen with a torsion handle and a cylindrical specimen. The bonding surface of the socket joint is parallel to the common axis of the specimen. The torsion shear force is transmitted to the bonding surface through the specimen axis until the bonding surface of the specimen is damaged. The torsion shear strength of the socket joint is calculated based on the maximum torsion shear strength per unit bonding area. 3 Test pieces and preparation of test specimens 3.1 Test pieces The test pieces shall be bonded together using R,000. The shape and size tolerances of the test pieces are shown in Figures 1 and 2. Non-gas test specimens Approved by State Technical Supervision Bureau on January 2, 1994 and implemented on October 1, 1994 3.2 Preparation of test specimens GR/T 14903-94 Figure 2 Typical test (material properties and preparation) 3.2-1 The pretreatment method of the test piece bonding surface, the proportion of the adhesive, the coating and the test specimen preparation process, if there are no special requirements, shall be determined in accordance with the relevant regulations.
3.2.2 The specimen with the torsion handle is put into the shape of the sample and the commercial specimen. In the gap between the specimen and the torsion handle, the outer conical surface of the specimen handle and the inner surface of the two simple modified parts are the positioning surfaces. The positioning surfaces do not require adhesive. The center positioning and curing tools are not required.
3.2.3 When the specimen is cured, the specimen should be placed vertically and the cylindrical specimen with the torsion handle should be placed vertically. The lower end of the specimen should be at least 3.2.4 The number of specimens
should be no less than the number of test racks under normal circumstances. 4 Instruments and equipment
The test sensor can ensure a stable torsion speed. The test platform used for the test is within the scope of the test load and the test load is within the scope of the test load.
5 Test environment
In the test environment, the humidity is 100% and the test cycle is 600°. 6 Test steps
6.1 The test specimen is placed under the filter. The test effect is greater than 1°. The test machine is placed at an angle of 21*mm to the test specimen. The test specimen is sheared. The test specimen is required to withstand the shear force of the test specimen.
6.2 Record the following types of test specimens: interface damage, internal damage, or combined damage. 7 Test results
The width of the wire is calculated according to formula (1):
The torsional shear strength of the joint, MPaF
The product of the joint resistance of the specimen, m\,
H/14903-94
The diameter of the joint of the brown-shaped specimen with a torque handle: mL—The length of the joint of the simple specimen with a torque handle, Ⅱ; The torque value indicated by the torque machine,·m.
Test report
The test report should include the following contents:
Name of inorganic adhesive, brand, production unit, production batch number, enterprise production date, processing code, code:
Storage used in the test, cavity connection table, processing method; sample preparation process;
Test conditions, damage type:
Test results:wwW.bzxz.Net
Testing machine model:
Testing unit, test date:
Additional remarks: